没有。 |
测试项目 |
健康)状况 |
材料 |
遵循的标准(如果有) |
类别:标准(请致电询价) |
1个 |
空气透过率
(差压法) |
23°C,0%RH |
电影/片材 |
ISO 2556-1974
ISO 15105-1:2007
ASTM D1434-1982(2009)e1 |
2 |
空气透过率
(等压方式) |
23°C,0%RH |
电影/片材 |
ASTM D3985-2005(2010)e1
ASTM F1927-2007
ISO 15105-2:2003
ASTM F2622-08(2013) |
3 |
氧气透过率
(差压法) |
23°C,0%RH |
电影/片材 |
ISO 2556-1974
ISO 15105-1:2007
ASTM D1434-1982(2009)e1 |
4 |
氧气透过率
(等压法) |
23°C,0%RH |
电影/片材 |
ASTM D3985-2005(2010)e1
ASTM F1927-2007
ISO 15105-2:2003
ASTM F2622-08(2013) |
5 |
二氧化碳透过率
(差压法) |
23°C,0%RH |
电影/片材 |
ISO 2556-1974
ISO 15105-1:2007
ASTM D1434-1982(2009)e1 |
6 |
氮气透过率 |
23°C,0%RH |
电影/片材 |
ISO 2556-1974
ISO 15105-1:2007
ASTM D1434-1982(2009)e1 |
7 |
氧气透过率(容器) |
23°C,0%RH |
容器 |
ASTM F1307-2002(2007)
ASTM D3985-2005(2010)e1
ASTM F1927-2007
ISO 15105-2:2003
ASTM F2622-08(2013) |
8 |
Air Transmission Rate (Container) |
23°C, Ambient |
Container |
ASTM F1307-2002(2007)
ASTM D3985-2005(2010)e1
ASTM F1927-2007
ISO 15105-2:2003
ASTM F2622-08(2013) |
9 |
Water Vapor Transmission Rate
(Gravimetric/Dish Method) |
38°C, 90%RH |
Film/Sheeting |
ISO 2528-1995
ASTM E96/E96M-2012
TAPPI T448 OM-09 |
10 |
Water Vapor Transmission Rate
(Electrolytic Detection Sensor Method) |
38°C, 90%RH |
Film/Sheeting |
ISO 15106.3-2003 |
11 |
Water Vapor Transmission Rate
(Infrared Detection Sensor Method) |
38°C, 90%RH |
Film/Sheeting |
ASTM F1249-13
ISO 15106.2-2003
TAPPI T557 wd-04 |
12 |
Water Vapor Transmission Rate
(Humidity Detection Sensor Method) |
38°C, 90%RH |
Film/Sheeting |
ASTM E398-13
ISO 15106.1-2003 |
13 |
Water Vapor Transmission Rate of Container
(Electrolytic Detection Sensor Method) |
38°C, 90%RH |
Container |
ISO 15106.3-2003 |
14 |
Water Vapor Transmission Rate of Container
(Infrared Detection Sensor Method) |
38°C, 90%RH |
Container |
ASTM F1249-13
ISO 15106.2-2003 |
15 |
Oxygen Transmission Rate after Flex
(Differential Pressure Method) |
23°C, 0%RH |
Film/Sheeting |
ISO 2556-1974
ISO 15105-1:2007
ASTM D1434-1982(2009)e1 |
16 |
Oxygen Transmission Rate after Flex
(Equal Pressure Method) |
23°C, 0%RH |
Film/Sheeting |
ASTM D3985-2005(2010)e1
ASTM F1927-2007
ISO 15105-2:2003
ASTM F2622-08(2013) |
17 |
Nitrogen Transmission Rate after Flex
(Differential Pressure Method) |
23°C, 0%RH |
Film/Sheeting |
ISO 2556-1974
ISO 15105-1:2007
ASTM D1434-1982(2009)e1 |
18 |
Carbon Dioxide Transmission Rate after Flex
(Differential Pressure Method) |
23°C, 0%RH |
Film/Sheeting |
ISO 2556-1974
ISO 15105-1:2007
ASTM D1434-1982(2009)e1 |
19 |
Air Transmission Rate after Flex
(Differential Pressure Method) |
23°C, 0%RH |
Film/Sheeting |
ISO 2556-1974
ISO 15105-1:2007
ASTM D1434-1982(2009)e1 |
20 |
Water Vapor Transmission Rate after Flex
(Gravimetric/Dish Method) |
38°C, 90%RH |
Film/Sheeting |
ISO 2528-1995
ASTM E96/E96M-2012 |
21 |
Tensile Strength and Elongation Rate
(Lateral) |
23°C, 50%RH |
Film/Sheeting |
ISO 527-1:2012
ISO 527-3:1995
ASTM D882-2012 |
22 |
Tensile Strength and Elongation Rate
(Longitudinal) |
23°C, 50%RH |
Film/Sheeting |
ISO 527-1:2012
ISO 527-3:1995
ASTM D882-2012 |
23 |
Coefficient of Friction |
23°C, 50%RH |
Film/Sheeting |
ISO 8295-1995
ASTM D1894-2011e1 |
24 |
Mechanical Contacting Thickness Test |
23°C, 50%RH |
Film/Sheeting |
ISO 4593:1993
ASTM D374M-13
TAPPI T411 om-10
ISO 3034-2011
ISO 534-2011 |
25 |
Heat Seal Strength |
23°C, 50%RH |
Film/Sheeting |
ASTM F88/F88M-2009 |
26 |
Shrinking Force and Shrinkage Ratio
(Lateral) |
23°C, 50%RH |
Film/Sheeting |
ISO 14616-1997
DIN 53369-1976 |
27 |
Shrinking Force and Shrinkage Ratio
(Longitudinal) |
23°C, 50%RH |
Film/Sheeting |
ISO 14616-1997
DIN 53369-1976 |
28 |
Falling Dart Impact Energy |
23°C, 50%RH |
Film/Sheeting |
ISO 7765.1-1988
ASTM D1709-2009 |
29 |
Pendulum Impact Energy |
23°C, 50%RH |
Film/Sheeting |
ASTM D3420-2008a |
30 |
Tear Strength
(Elmendorf Method, Lateral) |
23°C, 50%RH |
Film/Sheeting |
ISO 6383.2-1983
ASTM D1922-2009
ISO1974-2012
TAPPI T414 om-12 |
31 |
Tear Strength
(Elmendorf Method, Longitudinal) |
23°C, 50%RH |
Film/Sheeting |
ISO 6383.2-1983
ASTM D1922-2009
ISO1974-2012
TAPPI T414 om-12 |
32 |
Tear Strength
(Trouser Tear Method, Lateral) |
23°C, 50%RH |
Film/Sheeting |
ISO 6383.1-1983
ASTM D1938-2008 |
33 |
Tear Strength
(Trouser Tear Method, Longitudinal) |
23°C, 50%RH |
Film/Sheeting |
ISO 6383.1-1983
ASTM D1938-2008 |
34 |
Tear Strength
(Right Angled Tear Method, Lateral) |
23°C, 50%RH |
Film/Sheeting |
ASTM D1004-2013 |
35 |
Tear Strength
(Right Angled Tear Method, Longitudinal) |
23°C, 50%RH |
Film/Sheeting |
ASTM D1004-2013 |
36 |
Peel Strength (Lateral) |
23°C, 50%RH |
Film/Sheeting |
ASTM F904-1998(2008) |
37 |
Peel Strength (Longitudinal) |
23°C, 50%RH |
Film/Sheeting |
ASTM F904-1998(2008) |
38 |
Hot Tack Strength |
As Required |
Film/Sheeting |
ASTM F2029-2008 |
39 |
Burst |
23°C, 50%RH |
Film/Sheeting |
ASTM F1140/F1140M-2013 |
40 |
Creep |
23°C, 50%RH |
Film/Sheeting |
ASTM F1140/F1140M-2013 |
41 |
Creep To Burst |
23°C, 50%RH |
Film/Sheeting |
ASTM F1140/F1140M-2013 |
42 |
Seal Strength of Open Package |
23°C, 50%RH |
Film/Sheeting |
ASTM F1140/F1140M-2013 |
43 |
Seal Strength with Expansion Restriction |
23°C, 50%RH |
Film/Sheeting |
ASTM F2054/F2054M-13 |
44 |
Residual Oxygen Analysis of Vacuum Package |
23°C, 50%RH |
Container |
/ |
45 |
Residual Oxygen Analysis of Vacuum Package |
23°C, 50%RH |
Film/Sheeting |
/ |
Category: Non-standard 1 (Please Call For Pricing) |
1 |
Helium Transmission Rate |
23°C, 0%RH |
Film/Sheeting |
ISO 2556-1974
ISO 15105-1:2007
ASTM D1434-1982(2009)e1 |
2 |
Oxygen Transmission Rate-Equal Pressure Method (Container) |
23°C, 100%RH |
Container |
ASTM F1307-2002(2007)
ASTM D3985-2005(2010)el
ASTM F1927-2007
ISO 15105-2:2003
ASTM F2622-08(2013) |
3 |
Oxygen Transmission Rate-Equal Pressure Method (Container) |
15-55°C, 35%-90%RH |
Container |
ASTM F1307-2002(2007)
ASTM D3985-2005(2010)el
ASTM F1927-2007
ISO 15105-2:2003
ASTM F2622-08(2013) |
4 |
Carbon Dioxide Transmission Rate-Differential Pressure Method |
23°C, 100%RH |
Film/Sheeting |
ISO 2556-1974
ISO 15105-1:2007
ASTM D1434-1982(2009)e1 |
5 |
Carbon Dioxide Transmission Rate-Differential Pressure Method |
5-95°C, 10%-90%RH |
Film/Sheeting |
ISO 2556-1974
ISO 15105-1:2007
ASTM D1434-1982(2009)e1 |
6 |
Nitrogen Transmission Rate-Differential Pressure Method |
23°C, 100%RH |
Film/Sheeting |
ISO 2556-1974
ISO 15105-1:2007
ASTM D1434-1982(2009)e1 |
7 |
Nitrogen Transmission Rate-Differential Pressure Method |
5-95°C,
10%-90%RH |
Film/Sheeting |
ISO 2556-1974
ISO 15105-1:2007
ASTM D1434-1982(2009)e1 |
8 |
Oxygen Transmission Rate-Differential Pressure Method |
23°C, 100%RH |
Film/Sheeting |
ISO 2556-1974
ISO 15105-1:2007
ASTM D1434-1982(2009)e1 |
9 |
Oxygen Transmission Rate-Differential Pressure Method |
5-95°C,
10%-90%RH |
Film/Sheeting |
ISO 2556-1974
ISO 15105-1:2007
ASTM D1434-1982(2009)e1 |
10 |
Air Transmission Rate-Differential Pressure Method |
23°C, 100%RH |
Film/Sheeting |
ISO 2556-1974
ISO 15105-1:2007
ASTM D1434-1982(2009)e1 |
11 |
Air Transmission Rate-Differential Pressure Method |
5-95°C,
10%-90%RH |
Film/Sheeting |
ISO 2556-1974
ISO 15105-1:2007
ASTM D1434-1982(2009)e1 |
12 |
Oxygen Transmission Rate-Equal Pressure Method |
23°C, 100%RH |
Film/Sheeting |
ASTM F1927-2007
ISO 15105-2:2003
ASTM D3985-2005(2010)e1 |
13 |
Oxygen Transmission Rate-Equal Pressure Method |
10-55°C,
35%-90%RH |
Film/Sheeting |
ASTM F1927-2007
ISO 15105-2:2003
ASTM D3985-2005(2010)e1 |
14 |
Water Vapor Transmission Rate-Gravimetric/Dish Method |
15-55°C,
35%-90%RH |
Film/Sheeting |
ISO 2528-1995
ASTM E96/E96M-2012
TAPPI T464 om-12 |
15 |
Water Vapor Transmission Rate-Electrolytic Detection Sensor Method |
38°C, 100%RH |
Film/Sheeting |
ISO 15106.3-2003 |
16 |
Water Vapor Transmission Rate-Electrolytic Detection Sensor Method |
15-55°C,
35%-90%RH |
Film/Sheeting |
ISO 15106.3-2003 |
17 |
Water Vapor Transmission Rate-Infrared Detection Sensor Method |
15-55°C,
35%-90%RH |
Film/Sheeting |
ASTM F1249-13
ISO 15106.2-2003
TAPPI T557 wd-04 |
18 |
Water Vapor Transmission Rate-Infrared Detection Sensor Method |
38°C, 100%RH |
Film/Sheeting |
ASTM F1249-13
ISO 15106.2-2003
TAPPI T557 wd-04 |
19 |
Water Vapor Transmission Rate-Humidity Detection Sensor Method |
15-55°C,
35%-90%RH |
Film/Sheeting |
ASTM E398-13
ISO 15106.1-2003 |
20 |
Water Vapor Transmission Rate-Electrolytic Detection Sensor Method (Container) |
38°C, 100%RH |
Container |
ISO 15106.3-2003 |
21 |
Water Vapor Transmission Rate-Electrolytic Detection Sensor Method (Container) |
15-55°C, 35%-90%RH |
Container |
ISO 15106.3-2003 |
22 |
Oxygen Transmission Rate after Flex-Differential Pressure Method |
23°C, 100%RH |
Film/Sheeting |
ISO 2556-1974
ISO 15105-1:2007
ASTM D1434-1982(2009)e1 |
23 |
Oxygen Transmission Rate after Flex-Differential Pressure Method |
5-95°C,
10%-90%RH |
Film/Sheeting |
ISO 2556-1974
ISO 15105-1:2007
ASTM D1434-1982(2009)e1 |
24 |
Oxygen Transmission Rate after Flex- Equal Pressure Method |
23°C, 100%RH |
Film/Sheeting |
ASTM F1927-2007
ISO 15105-2:2003
ASTM D3985-2005(2010)e1 |
25 |
Oxygen Transmission Rate after Flex-Equal Pressure Method |
10-55°C,
35%-90%RH |
Film/Sheeting |
ASTM F1927-2007
ISO 15105-2:2003
ASTM D3985-2005(2010)e1 |
26 |
Nitrogen Transmission Rate after Flex-Differential Pressure Method |
23°C, 100%RH |
Film/Sheeting |
ISO 2556-1974
ISO 15105-1:2007
ASTM D1434-1982(2009)e1 |
27 |
Nitrogen Transmission Rate after Flex-Differential Pressure Method |
5-95°C,
10%-90%RH |
Film/Sheeting |
ISO 2556-1974
ISO 15105-1:2007
Reference:
ASTM D1434-1982(2009)e1 |
28 |
Carbon Dioxide Transmission Rate after Flex-Differential Pressure Method |
23°C, 100%RH |
Film/Sheeting |
ISO 2556-1974
ISO 15105-1:2007
ASTM D1434-1982(2009)e1 |
29 |
Carbon Dioxide Transmission Rate after Flex-Differential Pressure Method |
5-95°C,
10%-90%RH |
Film/Sheeting |
ISO 2556-1974
ISO 15105-1:2007
ASTM D1434-1982(2009)e1 |
30 |
Coefficient of Friction |
Room temperature ~ 99.9°C |
Film/Sheeting |
ASTM D1894-2011e1 |
31 |
Stress at Definite Elongation (Longitudinal) |
Ambient |
Film/Sheeting |
ISO 527-1:2012
ISO 527-3:1995
ASTM D882-2012 |
32 |
Stress at Definite Elongation (Lateral) |
Ambient |
Film/Sheeting |
ISO 527-1:2012
ISO 527-3:1995
ASTM D882-2012 |
33 |
Air Transmission Rate-Equal Pressure Method |
23°C, 100%RH |
Container |
ASTM F1307-2002(2007)
ASTM D3985-2005(2010)el
ASTM F1927-2007
ISO 15105-2:2003
ASTM F2622-08(2013) |
34 |
Air Transmission Rate-Equal Pressure Method |
15-55°C,
35%-90%RH |
Container |
ASTM F1307-2002(2007)
ASTM D3985-2005(2010)el
ASTM F1927-2007
ISO 15105-2:2003
ASTM F2622-08(2013) |
Category: Non-standard 2 (Please Call For Pricing) |
1 |
Rotary Torque of Bottle Cap |
Ambient |
Container |
ASTM D2063/D2063M-2010(2012)
ASTM D3198-1997(2007)
ASTM D3474-1990(2012) |
2 |
Seal Performance (Negative Pressure Method) |
Ambient |
Film/Sheeting |
ASTM D3078-02(2013) |
3 |
Seal Performance (Negative Pressure Method) |
Ambient |
Container |
ASTM D3078-02(2013) |
4 |
Flex Durability of Film (Turpentine Method) |
Ambient |
Film/Sheeting |
ASTM F392/F392M-2011 |
5 |
Primary Adhesion |
Ambient |
Film/Sheeting |
/ |
6 |
Lasting Adhesion |
Ambient |
Film/Sheeting |
/ |
7 |
Ink Layer Fastness |
Ambient |
Film/Sheeting |
/ |
8 |
Headspace Oxygen and Carbon Dioxide Analysis |
Ambient |
Film/Sheeting |
/ |
9 |
Residual Oxygen Analysis of Glass Bottle and Metal Jar |
Ambient |
Container |
/ |
10 |
Steaming and Boiling Resistance |
Ambient |
Film/Sheeting |
/ |
11 |
Seal Performance after Steaming and Boiling (Negative Pressure Method) |
Ambient |
Film/Sheeting |
ASTM D3078-02(2013) |
12 |
Cold Resistance |
Ambient |
Film/Sheeting |
/ |
13 |
Transmittance |
Ambient |
Film/Sheeting |
ASTM D1003-2011e1 |
14 |
Haze |
Ambient |
Film/Sheeting |
ASTM D1003-2011e1 |
15 |
Heat Shrinkage Ratio (Lateral) |
Ambient |
Film/Sheeting |
ASTM D2732-2008 |
16 |
热收缩率(纵向) |
周围 |
电影/片材 |
ASTM D2732-2008 |
17 |
极端高温和低温下包装膜的气体透过率(数据拟合) |
按要求 |
电影/片材 |
/ |
18岁 |
密封温度,压力和停留时间 |
周围 |
电影/片材 |
ASTM F88 / F88M-2009
ASTM F2029-2008 |